Iranian Nanotechnology Society International Journal of Nanoscience and Nanotechnology 1735-7004 11 2 2015 06 01 Effect of Nitric acid on Particle Morphology of the Nano-TiO2 115 122 13474 EN M. Ramazani Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, I. R. Iran M. Farahmandjou Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, I. R. Iran T.P. Firoozabadi Department of Physics, Varamin Pishva Branch, Islamis Azad University, Varamin, I. R. Iran Journal Article 2014 12 19 <em>Nano-sized titanium dioxide TiO<sub>2</sub> powder was prepared by new wet chemical route from its precursor Titanium (IV) chloride (TiCl<sub>4</sub>) as precursor with isopropoxy alcohol in presence of nitric acid under ambient condition. </em><em>Their morphologies, phase compositions and components of the TiO<sub>2</sub> nanoparticles</em><em> were characterized by transmission electron microscopy (TEM), field emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), electron dispersive spectroscopy (EDS), Fourier transform infrared spectroscopy (FTIR) and UV-Vis spectrophotometer. The TEM results showed the as-synthesized TiO<sub>2</sub> formed in nanometer scale. The FE-SEM images showed that the size of TiO<sub>2</sub> nanoparicles decreased with increasing annealing temperature while the uniformity of size distribution decreased. The FE-SEM images also revealed that the size of annealed TiO<sub>2</sub> nanocrystals increased with increasing the value of nitric acid. The average grain size of anatase nanoparticles was obtained about 25nm. The crystal structure of the nanoparticles before and after annealing was analyzed by XRD analysis. When the calcinations increased above 550<sup>o</sup>C, the phase transformation of anatase to rutile occurred, but the anatase phase was still dominant. The sharp peaks in FTIR spectrum determined the purity of TiO<sub>2</sub> nanoparticles and absorbance peak of UV-Vis spectrum showed anatase phase at wavelength about 380 nm with band gap of 3.26 ev for as-prepared TiO<sub>2 </sub>and rutile phase at wavelength about 382 nm with band gap of 3.24 ev for annealed TiO<sub>2</sub> nanoparticles. The EDS spectrum showed peaks of titanium and oxygen. </em> Nano-TiO2 Wet chemical Synthesis Phase transition Anatase phase https://www.ijnnonline.net/article_13474_2225c699a36afb253a69074cad850b00.pdf